Tuff-Temp™ Plus Provisional Veneer, Crown & Bridge Resin, 5mL Automix Syringe, 8 Automix Tips, 3mL Glaze, Shade A3.5 Pulpdent TTP5A35

Features & Benefits:

• Tuff-Temp™ Plus Provisional Veneer, Crown & Bridge Resin is Dual Cure Material and has Improved Rubberized-Resin Chemistry.
• Strong, impact resistant rubberized-resin doesn't shrink or distort and grips the tooth tightly.
• Virtually eliminates fractures and debonding.
• Grinds and powders during trimming without softening or distorting. Margins are perfect.
• The light cure option produces a full strength restoration on demand and is ideally suited for use with a clear vinyl polysiloxane template.
• Flexural Strength / Deflection at Break.
• Tuff-Temp™ Plus exhibits very high flexural strength without brittleness. Its deflection at break, the key indicator of toughness, is 50% to 100% greater than bis-acrylics.
• Tuff-Temp Provisional Glaze is a light cure glaze with the same proprietary rubberized-urethane chemistry that provides enhanced esthetics and patient satisfaction during temporization.
• Tough and resilient.
• Impact and fracture resistant.
• Tight fitting temps grip teeth securely.
• Greatly reduces breakage and cementation failures.
• Grinds and powders without softening.
• Trims to crisp, perfect margins.
• Does not gum up finishing instruments.
• Self-cure with fast light cure option.
• Enhanced esthetics.
• Faster setting time.
• Snap set.
• Fluorescence added.
• Includes Tuff-Temp Plus 5mL automix syringe, 8 automix tips, 3mL Tuff-Temp Glaze, Shade A35 (For A3.5).
• Tuff-Temp™ Plus - Physical Properties:
  • Working time: 45 seconds.
  • Initial self-cure setting time: 2 minutes from start of mix (75 seconds after insertion in the mouth).
  • Final self-cure setting time: 4:45 minutes from beginning of mix.
  • Light cure setting time: 20 seconds (halogen light).
  • Flexural strength: 77 MPa.
  • Compressive strength: 200 MPa.
  • Deflection at break: 2.9 mm.
  • Vickers Hardness: 514 MPa.

Application:

• For Dental Restoration Procedures.